PC/PTFE LNP™ LUBRICOMP™ DBL349E-BK
66
- Properties:Filler: Glass beads
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | 内部方法 | 0.50到0.70 % | |
| Water absorption rate | ISO62 | 0.13 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile strain | ISO527-2/5 | 3.1 % | |
| ISO527-2/5 | 4.6 % | ||
| Bending modulus 1 | ISO178 | 2900 Mpa | |
| Bending stress 2 | ISO178 | 76.0 Mpa | |
| ASTMD3702Modified | 0.50 | ||
| Fracture bending strain 3 | ISO178 | 5.3 % | |
| Wear factor - Washer | ASTMD3702Modified | 94.0 10^-10in^5-min/ft-lb-hr | |
| Tensile modulus | ISO527-2/1 | 2800 Mpa | |
| Tensile stress | ISO527-2/5 | 42.0 Mpa | |
| ISO527-2/5 | 40.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam gap impact strength 4 | ISO180/1A | 6.0 kJ/m² | |
| Unscented Izod Impact Strength 5 | ISO180/1U | 25 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 1.8MPa, Unanealed, 64.0mm span | ISO75-2/Af | 130 °C | |
| ISO11359-2 | 6E-05 cm/cm/°C | ||
| ISO11359-2 | 6.9E-05 cm/cm/°C | ||
| 0.45MPa, Unanealed, 64.0mm span | ISO75-2/Bf | 137 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.