Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | GB/T 2914 | 0.02 |
| Other performance | Test Condition | Test Method | Test Result |
|---|
| Wear amount | | GB/T 3960 | 4.0 mg/120min |
| Wear scar width | | GB/T 3960 | 5.0 mm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| coefficient of friction | | GB/T 3960 | 0.35 |
| Impact strength of cantilever beam gap | | GB/T 1843 | 10 kJ/m² |
| Flexural modulus | | GB/T 9341 | 1.4×10⁴ Mpa |
| bending strength | | GB/T 9341 | 220 Mpa |
| elongation at break | | GB/T 1040 | 1.2 |
| tensile strength | | GB/T 1040 | 145 Mpa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| electric strength | | GB/T 1408 | 16 KV/mm |
| dielectric constant | | GB/T 1409 | 4 |
| Surface Resistivity | | GB/T 1410 | 5 ×10¹⁴ Ω |
| Volume resistivity | | GB/T 1410 | 5 ×10¹⁵ Ω·m |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| Mold Shrinkage | | GB/T 15585 | 0.25/0.60 |
| density | | GB/T 1033 | 1.71 g/cm³ |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Flame retardancy | | GB/T UL94 | V-0 |
| Heat distortion temperature | | GB/T 1634 | 265 ℃ |
| melting point | | GB/T 4608 | 282 ℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.