Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.54 g/cm³ |
| Water absorption rate | | ASTMD570 | 0.12 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Limiting Oxygen Index | | ASTMD2863 | 20 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | Break | ASTM D790 | 200 MPa |
| tensile strength | Break | ASTMD638 | 140 MPa |
| elongation | Break | ASTMD638 | 2.0 % |
| Flexural modulus | | ASTMD790 | 9800 MPa |
| bending strength | | ISO 178 | 200 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179 | 8.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179 | 40 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTMD257 | 1E+16 ohms·cm |
| dielectric strength | | ASTMD149 | 25 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 1 |
| Compared to the Leakage Tracking Index (CTI) | | ASTM D3638 | PLC 1 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTMD648 | 220 °C |
| Heat distortion temperature | | ASTMD648 | 205 °C |
| melting temperature | | ISO 11357-3 | 225 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.