Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO 1133 | 3.0 g/10min |
| Environmental stress cracking resistance | | ASTM D1693B | >1000 hr |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 868 | 43 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | ASTM D2457 | 82 |
| Haze ratio | | ASTM D1003A | 2.0 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Puncture Resistance | | 内部方法 | 26.5 J/cm |
| Initial sealing temperature | | ASTMF88 | 80 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | | ISO R527-1966 | 820 % |
| Flexural modulus | | ISO 178 | 72.0 Mpa |
| tensile strength | | ISO R527-1966 | 31.0 Mpa |
| film | Test Condition | Test Method | Test Result |
|---|
| Secant modulus | | ASTM D882 | 65.0 Mpa |
| Dart impact | | ASTM D1709 | >32 g |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| brittle temperature | | ASTM D746 | <-76.0 °C |
| vicat | | ISO 306/A | 80.0 °C |
| melting temperature | | ISO 11357 | 96.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.