Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.05 g/cm³ |
| density | | | 1.057 g/cm³ |
| density | | | 1.027 g/cm³ |
| Contractility | | | 0.20 % |
| Contractility | | | 0.20 % |
| Contractility | | | 0.20 % |
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| | | 按重量计算的混合比:100,按容量计算的混合比:100 |
| | | 按重量计算的混合比:90,按容量计算的混合比:93 |
| Shelf Life | | 26 wk |
| | | 6.0到8.0 hr |
| | | 15.0 min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ASTMD2240 | 80到84 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| CureTime | | | 5.0到7.0 day |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTMD638 | 1790 MPa |
| tensile strength | Yield | ASTMD638 | 45.9 MPa |
| elongation | Yield | ASTMD638 | 65 % |
| Flexural modulus | | ASTMD790 | 2210 MPa |
| bending strength | | ASTMD790 | 75.8 MPa |
| Compression Modulus | | ASTMD695 | 2410 MPa |
| compressive strength | | ASTMD695 | 57.6 MPa |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|
| Brookfield viscosity | | | 600到700 mPa·s |
| Brookfield viscosity | | | 550到650 mPa·s |
| Brookfield viscosity | | | 550 mPa·s |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 53 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | | 9E-05 |
| | ASTMD648 | 70.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare