ABS POLYLAC® PA-764B TAIWAN CHIMEI
704
- Properties:heat-resisting
- Usages:Home appliance componentsFitness equipmentElectronic fieldElectrical field
- Certificates:UL
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | ASTM D1238/ISO 1133 | 2.8 | g/10min | |
| ASTM D1238/ISO 1133 | 28 | g/10min | ||
| density | ASTM D792/ISO 1183 | 1.16 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 16（3.0） | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 12(2.2) | kg·cm/cm(J/M)ft·lb/in | ||
| tensile strength | ASTM D638/ISO 527 | 400（5，810） | kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 20 | % | |
| Rockwell hardness | ASTM D785 | R-102 | ||
| Bending modulus | ASTM D790/ISO 178 | 23000（32000） | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 660（9，370） | kg/cm²(MPa)[Lb/in²] |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Combustibility (rate) | UL94 | 2.5mm，V-0 3.2mm，5VA | ||
| Hot deformation temperature | ASTM D648/ISO 75 | 93（199） | ℃（℉） | |
| ASTM D648/ISO 75 | 80（176） | ℃（℉） | ||
| vicat softening point | ASTM D1525/ISO R306 | 101（214） | ℃（℉） |
| Processing conditions | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dry conditions | 80°C下烘料约2~3小时 | |||
| Processing temperature | 220~180 | °C | ||
| 190~220 | °C | |||
| 180~220°C | °C | |||
| Mold temperature | 40~70°C | °C | ||
| pressure | 20~50kg/cm² | Mpa | ||
| 5~10kg/cm² | Mpa | |||
| 50~80kg/cm² | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.