Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.11 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 1.6 g/10min |
| Shrinkage rate | | 内部方法 | 0.40 % |
| Water absorption rate | Equilibrium | ASTM D570 | 0.090 % |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ASTM D542 | 1.550 |
| transmissivity | | ISO 13468-1 | 92.0 % |
| Haze ratio | | ISO 14782 | 0.20 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Break | ISO 527-2/5 | 64.0 MPa |
| Nominal tensile fracture strain | | ISO 527-2/5 | 5.0 % |
| Flexural modulus | | ISO 178 | 3400 MPa |
| bending strength | | ISO 178 | 113 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179 | 2.0 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Hot deformation temperature (HDT) | | ISO 75-2/Af | 79.0 °C |
| vicat | | ISO 306/B | 100 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.