Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | % | 0.10to0.31 |
| saturation | | % | 3.5to5.0 |
| density | | g/cm³ | 1.28to1.85 |
| balance | | % | 1.2to1.5 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | | 222.76to370.34 Mpa |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | | 144.83to292.41 Mpa |
| Tensile strain | | % | 1.9to3.1 |
| Tensile modulus | | | 8206.9to28000.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | kJ/m² | 3.065to3.343 |
| Impact strength of simply supported beam without notch | | kJ/m² | 11.143to19.964 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ohms·cm | 1.0E+12到1.0E+14 |
| dielectric strength | | V/mil | 840 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| horizontal | | mm/mm/°C | 68.6E-5-127.0E-5 |
| flow | | mm/mm/°C | 142.2E-5-203.2E-5 |
| melting temperature | | °C | 260 |
| Continuous use temperature | | °C | 110to220 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.