Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Thermosetting components | | | 按重量计算的混合比:50.按容量计算的混合比:50 |
| Thermosetting mixed viscosity | | ASTM D4878 | 2550 cP |
| stripping time | | | 60to120 min |
| GelTime | | ASTM D2971 | 25.0 min |
| Thermosetting components | | | 按重量计算的混合比:100.按容量计算的混合比:100 |
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTM D2566 | 0.10to0.30 % |
| Weight Percubicinch | | | 17 g |
| density | | ASTM D4669 | 1.10 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 65 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ThermalShockTest | | | Pass |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Suspended wall beam without notch impact strength | | ASTM D256 | 无断裂 |
| Impact strength of cantilever beam gap | | ASTM D256 | 120 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 172 MPa |
| tensile strength | | ASTM D638 | 22.8 MPa |
| elongation | Break | ASTM D638 | 100 % |
| Flexural modulus | | ASTM D790 | 283 MPa |
| bending strength | | ASTM D790 | 18.6 MPa |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tear strength | | ASTM D624 | 78.8 kN/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 5.1E+15 ohms·cm |
| dielectric strength | | ASTM D149 | >14 kV/mm |
| dielectric constant | | ASTM D150 | 3.30 |
| dielectric constant | | ASTM D150 | 3.00 |
| Dissipation Factor | | ASTM D150 | 0.037 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| thermal conductivity | | | 0.22 W/m/K |
| Usage temperature | | | 135 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.