Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 0.930 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 8.0 g/10min |
| Shrinkage rate | | ASTM D955 | 1.5to1.9 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 90 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-2 |
| UL flame retardant rating | | | 130 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 29.4 Mpa |
| elongation | | ASTM D638 | 200 % |
| Flexural modulus | | ASTM D790 | 1470 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 69 J/m |
| injection | Test Condition | Test Method | Test Result |
|---|
| Temperature at the rear of the barrel | | | 170 到 180 °C |
| Temperature in the middle of the barrel | | | 180 到 200 °C |
| Temperature at the front of the material cylinder | | | 180 到 200 °C |
| Spray nozzle temperature | | | 190 到 210 °C |
| Temperature | | | 40 到 70 °C |
| Injection Pressure | | | 39.2 到 78.5 Mpa |
| Back pressure | | | 0.490 到 1.96 Mpa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 120 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare
View Prices