Technical Data Sheet
| other | Test Condition | Test Method | Test Result |
|---|
| | | 高冲击性押出级 |
| purpose | | | 冰箱板材 |
| processability | Test Condition | Test Method | Test Result |
|---|
| Dry conditions | | | 80℃，2~3小时 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D-1238 | 0.5 g/10min |
| melt mass-flow rate | | ISO 1133 | 5 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638/ISO 527 | 420(5950) kg/cm²(MPa)[Lb/in²] |
| elongation | | ASTM D638/ISO 527 | 30 % |
| Rockwell hardness | | ASTM D785 | R-108 |
| Flexural modulus | | ASTM D790/ISO 178 | 2.2(3.1) kg/cm²(MPa)[Lb/in²] |
| bending strength | | ASTM D790/ISO 178 | 620(8800) kg/cm²(MPa)[Lb/in²] |
| Izod notch impact strength | | ASTM D256/ISO 179 | 33(6.1) kg·cm/cm(J/M)ft·lb/in |
| Izod notch impact strength | | ASTM D256/ISO 179 | 37.5(6.9) kg·cm/cm(J/M)ft·lb/in |
| IZOD impact strength | | ASTM D-256 | 35 kg.cm/cm |
| bending strength | | ASTM D-790 | 620 kg/cm2 |
| | ASTM D-790 | 40 % |
| Flexural modulus | | ASTM D-790 | 2.1 104kg/cm2 |
| Rockwell hardness | | ASTM D-785 | 102 R |
| Tensile strength | | ASTM D-638 | 390 kg/cm2 |
| IZOD impact strength | | ASTM D-256 | 40 kg.cm/cm |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 1.03 |
| melt mass-flow rate | | ASTM D1238/ISO 1133 | 0.8 g/10min |
| melt mass-flow rate | | ASTM D1238/ISO 1133 | 9 g/10min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Combustibility (rate) | | UL94 | 1.6mm |
| | ASTM D648/ISO 75 | 97(207) ℃（℉） |
| | ASTM D648/ISO 75 | 86(187) ℃（℉） |
| vicat | | ASTM D1525/ISO R306 | 103(217) ℃（℉） |
| | ASTM D-648 | 97(207) ℃(°F) |
| | ASTM D-648 | 87(189) ℃(°F) |
| vicat | | ASTM D-1525 | 103(217) ℃(°F) |
| combustibility | | File NO.E196075 | 1/16"HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.