Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ASTM D570 | 0.020 % |
| density | | ASTM D792 | 2.00 g/cm³ |
| Shrinkage rate | | ASTM D955 | 0.25 % |
| Shrinkage rate | | ASTM D955 | 1.0 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTM D785 | 100 |
| Rockwell hardness | R-Scale | ASTM D785 | 121 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 21000 MPa |
| tensile strength | | ASTM D638 | 120 MPa |
| elongation | Break | ASTM D638 | 0.80 % |
| elongation at break | | ASTM D790 | 1.2 % |
| Flexural modulus | | ASTM D790 | 20000 MPa |
| bending strength | | ASTM D790 | 175 MPa |
| compressive strength | | ASTM D695 | 150 MPa |
| Poisson's ratio | | | 0.33 |
| coefficient of friction | Steel - Dynamic | ASTM D1894 | 0.35 |
| coefficient of friction | Steel - Static | ASTM D1894 | 0.35 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 70 J/m |
| Suspended wall beam without notch impact strength | | ASTM D256 | 230 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 1E+16 ohms·cm |
| dielectric strength | | ASTM D149 | 16 kV/mm |
| dielectric constant | | ASTM D150 | 5.00 |
| Dissipation Factor | | ASTM D150 | 7E-03 |
| arc resistance | | ASTM D495 | 180 sec |
| Compared to the Leakage Tracking Index (CTI) | | ASTM D3638 | PLC 2 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 265 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 1.7E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ASTM D696 | 1.7E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.