Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
density | | ASTM D792 | 0.934to0.938 g/cm³ |
density | | ISO 1183 | 0.934to0.940 g/cm³ |
density | | ASTM D1505 | 0.914to0.959 g/cm³ |
melt mass-flow rate | | ASTM D1238 | 3.9to6.1 g/10min |
melt mass-flow rate | | ISO 1133 | 3.3to6.1 g/10min |
Environmental stress cracking resistance | | ASTM D1693 | 27.9to1000 hr |
hardness | Test Condition | Test Method | Test Result |
---|
Shore hardness | | ASTM D2240 | 60to65 |
Shore hardness | | ISO 868 | 55to57 |
optical performance | Test Condition | Test Method | Test Result |
---|
gloss | | ASTM D2457 | 50to88 |
Haze ratio | | ASTM D1003 | 3.0to18 % |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
Tensile modulus | | ISO 527-2 | 646to758 MPa |
tensile strength | | ASTM D638 | 17.9to20.0 MPa |
tensile strength | | ISO 527-2 | 18.0to22.0 MPa |
Tensile strain | | ISO 527-2 | 11to12 % |
Tensile strain | | ASTM D638 | 380to1000 % |
Tensile strain | | ISO 527-2 | 88to1000 % |
Flexural modulus | | ASTM D790 | 556to862 MPa |
Flexural modulus | | ISO 178 | 698to803 MPa |
film | Test Condition | Test Method | Test Result |
---|
film thickness | | | 20to26 µm |
Thermal performance | Test Condition | Test Method | Test Result |
---|
brittle temperature | | ASTM D746 | -70.2--70.0 °C |
vicat | | ISO 306 | 113to118 °C |
melting temperature | | | 126to128 °C |
Heat distortion temperature | | ASTM D648 | 63.9to71.5 °C |
Heat distortion temperature | | ISO 75-2/B | 64.8to68.2 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.