Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.18 g/cm³ |
| melt mass-flow rate | | ISO1133 | 1.0 g/10min |
| Shrinkage rate | | | 0.40到0.70 % |
| Water absorption rate | | ISO62 | 0.30 % |
| Average particle size | | | 600 µm |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO2039-2 | 99 |
| | ISO2039-1 | 190 MPa |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ISO489 | 1.490 |
| transmissivity | | ASTMD1003 | 92.0 % |
| Haze ratio | | ASTMD1003 | 0.40 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Hot filament ignition temperature | | IEC60695-2-13 | 650 °C |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| CrazeResistance | | 内部方法 | >1.0 hr |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Bending stress | | ISO178 | 120 MPa |
| Tensile stress | | ISO527-2 | 85.0 MPa |
| Tensile strain | Break | ISO527-2 | 5.0 % |
| Flexural modulus | | ISO178 | 3400 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 2.2 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 23 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 2.1 kJ/m² |
| Multi axis Instrumented Impact Energy | | ISO6603-2 | 0.600 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO75-2/B | 106 °C |
| Heat distortion temperature | | ISO75-2/A | 102 °C |
| vicat | | ISO306/A | 117 °C |
| vicat | | ISO306/B | 109 °C |
| | ASTME831 | 7.1E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.