Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| shelf-life | | | 26 wk |
| Thermosetting mixed viscosity | | ASTM D2393 | 975 cP |
| stripping time | | | 300to360 min |
| Post curing time | | | 16 hr |
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.31 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 80 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 1810 MPa |
| tensile strength | | ASTM D638 | 44.1 MPa |
| elongation | Break | ASTM D638 | 4.6 % |
| Flexural modulus | | ASTM D790 | 2270 MPa |
| bending strength | | ASTM D790 | 78.9 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 29 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 90.6 °C |
| Heat distortion temperature | | ASTM D648 | 83.9 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.