Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 30 g/10 min |
| Shrinkage rate | | ASTM D955 | 0.40 - 0.70 % |
| Shrinkage rate | | ASTM D955 | 0.40 - 0.70 % |
| Shrinkage rate | | ISO 294-4 | 0.40 - 0.70 % |
| Shrinkage rate | | ISO 294-4 | 0.40 - 0.70 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 118 |
| Rockwell hardness | | ISO 2039-2 | 119 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-2 |
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 2000 Mpa |
| Tensile modulus | | ISO 527-2/50 | 2000 Mpa |
| tensile strength | | ASTM D638 | 58.0 Mpa |
| tensile strength | | ISO 527-2/50 | 55.0 Mpa |
| tensile strength | | ASTM D638 | 59.0 Mpa |
| tensile strength | | ISO 527-2/50 | 60.0 Mpa |
| elongation | | ASTM D638 | 100 % |
| elongation | | ISO 527-2/50 | 100 % |
| Flexural modulus | | ASTM D790 | 2100 Mpa |
| Flexural modulus | | ISO 178 | 2100 Mpa |
| bending strength | | ASTM D790 | 78.0 Mpa |
| bending strength | | ISO 178 | 80.0 Mpa |
| injection | Test Condition | Test Method | Test Result |
|---|
| Hot air dryer | | | 100 to 120 °C |
| Vacuum dryer | | | 100 to 120 °C |
| Hot air dryer | | | 4.0 hr |
| Vacuum dryer | | | 4.0 hr |
| Suggested maximum moisture content | | | 0.020 % |
| Temperature at the rear of the barrel | | | 220 to 260 °C |
| Temperature in the middle of the barrel | | | 240 to 280 °C |
| Temperature at the front of the material cylinder | | | 260 to 300 °C |
| Spray nozzle temperature | | | 260 to 300 °C |
| Temperature | | | 70 to 100 °C |
| Injection Pressure | | | 68.6 to 127 Mpa |
| Back pressure | | | 0.981 to 1.96 Mpa |
| screw speed | | | 60 to 90 rpm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 126 °C |
| Heat distortion temperature | | ISO 75-2/A | 123 °C |
| vicat | | ISO 306/B50 | 142 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.