PC RAMLLOY PZF101
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 1.20 g/cm³ | |
| ISO 1183 | 1.20 g/cm³ | ||
| melt mass-flow rate | ASTM D1238 | 18 g/10min | |
| ISO 1133 | 18 g/10min | ||
| Shrinkage rate | ASTM D955 | 3E-03 % | |
| ISO 2577 | 3E-03 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 1800 MPa | |
| ISO 527-2 | 1800 MPa | ||
| tensile strength | Yield | ASTM D638 | 50.0 MPa |
| Yield | ISO 527-2 | 50.0 MPa | |
| elongation | Break | ASTM D638 | 140 % |
| Tensile strain | Break | ISO 527-2 | 140 % |
| Flexural modulus | ASTM D790 | 1700 MPa | |
| ISO 178 | 1700 MPa | ||
| bending strength | ASTM D790 | 75.0 MPa | |
| ISO 178 | 75.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 550 J/m | |
| ASTM D256 | 750 J/m | ||
| ISO 180 | 55 kJ/m² | ||
| ISO 180 | 65 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 115 °C | |
| ISO 75-2/B | 115 °C | ||
| ASTM D648 | 90.0 °C | ||
| ISO 75-2/A | 90.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.