PBT

PBT Sunny® PBT EB220 Guangdong Shunde Shunyan New Material Co., Ltd.

Properties:
Filler glass fiber reinforced material 20% filler by weight
Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C5	ISO 180/1A	7.2 kJ/m²
	Impact strength of cantilever beam gap	23°C	ASTM D256	77 J/m
		Impact strength of cantilever beam gap	23°C	ASTM D256	77 J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C5	ISO 180/1A	7.2 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.6mm	UL 94	V-0
	UL flame retardant rating	3.2mm	UL 94	V-0
		UL flame retardant rating	1.6mm	UL 94	V-0
		UL flame retardant rating	UL flame retardant rating	3.2mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
elongation	Break3	ASTM D638	2.8 %
bending strength	--4	ISO 178	150 MPa
bending strength	bending strength	50.0mmSpan	ASTM D790	145 MPa
Bending modulus	--4	ISO 178	4200 MPa
Bending modulus	Bending modulus	50.0mmSpan	ASTM D790	4070 MPa
elongation	Break	ISO 527-2/5	3.0 %
Bending modulus	--4	ISO 178	4200 MPa
tensile strength	--	ISO 527-2/5	110 MPa
tensile strength	tensile strength	--3	ASTM D638	110 MPa
bending strength	--4	ISO 178	150 MPa
elongation	Break3	ASTM D638	2.8 %
bending strength	50.0mmSpan	ASTM D790	145 MPa
Bending modulus	50.0mmSpan	ASTM D790	4070 MPa
elongation	Break	ISO 527-2/5	3.0 %
tensile strength	--3	ASTM D638	110 MPa
tensile strength	tensile strength	--	ISO 527-2/5	110 MPa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTMD648	185 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTMD648	185 °C

Physical properties	Test Condition	Test Method	Test Result
density	--2	ASTM D792	1.52 g/cm³
Shrinkage rate	MD:23°C	ASTM D955	0.40to0.70 %
melt mass-flow rate	250°C/2.16kg	ASTMD1238	30 g/10min
Water absorption rate	Equilibrium,23°C	ASTM D570	0.080 %
density	23°C	ISO 1183	1.52 g/cm³
Shrinkage rate	23°C	ISO 294-4	0.40to0.70 %
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.080 %
density	--2	ASTM D792	1.52 g/cm³
density	density	23°C	ISO 1183	1.52 g/cm³
melt mass-flow rate	250°C/2.16kg	ASTMD1238	30 g/10min
Shrinkage rate	MD:23°C	ASTM D955	0.40to0.70 %
Shrinkage rate	Shrinkage rate	23°C	ISO 294-4	0.40to0.70 %
Water absorption rate	Equilibrium,23°C	ASTM D570	0.080 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.080 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.