ABS/PBT KU2-7604 LANXESS GERMANY

Form：Granules | Grade：Flame retardant

Properties:

Low warpageFlame retardant

Typical Applications:

Electrical and electronic equipment

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electrical and electronic equipment
Properties:	Low warpage \| Flame retardant

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	NoBreak
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	NoBreak
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.8mm	UL 94	V-0
Burning wire flammability index	0.8mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	0.8mm	IEC 60695-2-13	775	°C
	Hot filament ignition temperature	1.6mm	IEC 60695-2-13	775	°C
	Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC 60695-2-13	775	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Yield,23°C	ISO 527-2/50	45.0	Mpa
Tensile strain	Yield,23°C	ISO 527-2/50	3.5	%
Nominal tensile fracture strain	23°C	ISO 527-2/50	>20	%
Bending modulus	23°C	ISO 178/A	2000	Mpa
bending strength	3.5%Strain,23°C	ISO 178/A	65.0	Mpa
bending strength	bending strength	23°C4	ISO 178/A	70.0	Mpa
Bending strain	23°C	ISO 178/A	5.0	%
Tensile modulus	23°C	ISO 527-2/1	2000	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	1E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	1.1E-04	cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	100	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	75.0	°C
Vicat softening temperature		ISO 306/B120	115	°C
Melting temperature		ISO 11357-3	225	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Apparent density		ISO 60	0.80	g/cm³
Melt Volume Flow Rate (MVR)	260°C/5.0kg	ISO 1133	20.0	cm3/10min
Shrinkage rate	TD:250°C,2.00mm2	ISO 2577	0.80	%
	Shrinkage rate	TD:120°C,4hr,2.00mm3	ISO 2577	0.80	%
		Shrinkage rate	MD:250°C,2.00mm2	ISO 2577	0.80	%
		Shrinkage rate	Shrinkage rate	MD:120°C,4hr,2.00mm3	ISO 2577	0.80	%
Water absorption rate	Saturation,23°C	ISO 62	0.30	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.10	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test		ISO 2039-1	93.0	Mpa
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
ISO Shortcut		ISO 7792	PBT+PC.GFHLMPR.11-020

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.