PA6 ST-301 SHANGHAI CELLULOID

Form：Granules | Grade：Enhanced level

Properties:

Low temperature impact reGlass fiber reinforced

Typical Applications:

ShellTool productsParts box

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Shell \| Tool products \| Parts box
Properties:	Low temperature impact re \| Glass fiber reinforced

Certificates

No Data...

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			含弹性体.30%短玻纤增强。高抗冲.耐低温。
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength		ASTM D638/ISO 527	130	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	4140	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	150	kg/cm²(MPa)[Lb/in²]
Impact strength of cantilever beam gap	Unnotched	GB 1043	97	KJ/m
tensile strength	Break	GB 1040	130	Mpa
elongation		GB 1040	2	%
tensile strength	Yield	GB 1040	130	Mpa
bending strength		GB 1042	150	Mpa
Impact strength of cantilever beam gap	Notched	GB 1043	38	KJ/m
Bending modulus			4140	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	HDT	ASTM D648/ISO 75	200	℃（℉）
Melting temperature			215	℃（℉）
Hot deformation temperature	1.81MPa	GB 1634	200	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792/ISO 1183	1.36
Fiberglass content		GB 1033	30	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		ASTM D257/IEC 60093	1013	Ω.cm
Volume resistivity	Volume resistivity		GB 1044	10	Ω.cm
Surface resistivity		GB 1044	10	Ω

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.