Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| gloss | | ASTM D-2457 | >50 |
| other | Test Condition | Test Method | Test Result |
|---|
| notes | | | 吹塑 薄膜 光学 |
| purpose | | | 收缩薄膜.层压膜 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | | 3.4-4.6 g/10min |
| density | | | 0.922-0.926 g/cm |
| Other performance | Test Condition | Test Method | Test Result |
|---|
| Opening agent | | | 1650-1950 ppm |
| Dart impact | | ASTM D-1709 | >70 g |
| Anti-skid agent | | | 500-700 ppm |
| film thickness | | | 50 µm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527 | >9 N/mm |
| elongation at break | | ISO 527 | >200 % |
| elongation at break | | ISO 527 | >550 % |
| Elastic modulus | | ISO 527 | >200 N/mm |
| tensile strength | | ISO 527 | >18 Mpa |
| tensile strength | | ISO 527 | >10 Mpa |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 0.922-0.926 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | ISO 3146 | >110 °C |
| vicat | | ISO 306 | >90 °C |
| vicat | | ASTM D1525/ISO R306 | >90 ℃（℉） |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.