PPA HTN54G15HSLR BK031 DUPONT CANADA

Form：Granules | Grade：Enhanced level

Properties:

enhanceGlass fiber reinforcedTougheningFiller: Glass fiber reinf15% filler by weight

Typical Applications:

building materialsIndustrial applicationsAutomotive interior partsElectrical fieldElectronic field

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	building materials \| Industrial applications \| Automotive interior parts \| Electrical field \| Electronic field
Properties:	enhance \| Glass fiber reinforced \| Toughening \| Filler: Glass fiber reinf \| 15% filler by weight

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179/1eA	6.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-40°C	ISO 179/1eA	5.0	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	60	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning rate	1.00mm	ISO 3795	<100	mm/min
FMVSS flammability		FMVSS302	B
UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	HB
	UL flame retardant rating	0.8mm	IEC 60695-11-10,-20	HB
		UL flame retardant rating	1.5mm	UL 94	HB
		UL flame retardant rating	UL flame retardant rating	0.8mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	210	Mpa
Bending modulus		ISO 178	4900	Mpa
Tensile strain	Break	ISO 527-2	3.5	%
tensile strength	Break	ISO 527-2	125	Mpa
Tensile modulus		ISO 527-2	5500	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD：-40to23°C	ISO 11359-2	7E-05	cm/cm/°C
	Linear coefficient of thermal expansion	TD：--	ISO 11359-2	7.3E-05	cm/cm/°C
		Linear coefficient of thermal expansion	MD：-40to23°C	ISO 11359-2	3.4E-05	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：--	ISO 11359-2	3.4E-05	cm/cm/°C
Melting temperature		ISO 11357-3	300	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	230	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	277	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	MD	ISO 294-4	0.40	%
Shrinkage rate	Shrinkage rate	TD	ISO 294-4	0.70	%
density		ISO 1183	1.25	g/cm³
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		IEC 60093	1E+15	ohms·cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.