PVC Homopolymer VESTOLIT G M117 (120 Series)
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Apparent density | 0.46 g/cm³ | ||
| K-Value | 内部方法 | 74.0 | |
| intrinsic viscosity | 内部方法 | 1.2 | |
| Humidity Karl Fisher | 内部方法 | 0.040 % | |
| relative viscosity | 2.65 | ||
| density | ASTM D792 | 1.40 g/cm³ |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| gloss | 内部方法 | 92 % | |
| 内部方法 | 61 % | ||
| transmittance | 内部方法 | 94 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| North fineness | 内部方法 | 3.25 Hegman | |
| ResidualVinylChlorideMonomer | 内部方法 | <9 ppm | |
| Methanol extractable | 内部方法 | 2.2 % | |
| Polymerization rate | Microsuspension | ||
| gel temperature | 内部方法 | 65 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation at break | ASTM D638 | 20.1 MPa |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Brookfield viscosity | 内部方法 | 5.98 Pa·s | |
| 内部方法 | 4.80 Pa·s | ||
| 内部方法 | 6.40 Pa·s | ||
| 内部方法 | 6.45 Pa·s | ||
| Cut off the outflow | 内部方法 | 48.00 g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.