Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D-792 | 无水｜1.5 |
| density | | ASTM D-792 | 1.9%水｜- |
| Taber wear amount | | ASTM D-1044 | 无水｜30 mg/1000次 |
| Taber wear amount | | ASTM D-1044 | 1.9%水｜- mg/1000次 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ASTM D-570 | 无水｜0.9 % |
| Water absorption rate | | ASTM D-570 | 1.9%水｜- % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| IZOD impact strength | | ASTM D-256 | 1.9%水｜120 kg·cm/cm |
| flexural modulus | | ASTM D-790 | 无水｜122000 kg/cm2 |
| flexural modulus | | ASTM D-790 | 1.9%水｜72000 kg/cm2 |
| flexural modulus | | ASTM D-790 | 无水｜63000 kg/cm2 |
| flexural modulus | | ASTM D-790 | 1.9%水｜45000 kg/cm2 |
| flexural modulus | | ASTM D-790 | 无水｜140000 kg/cm2 |
| flexural modulus | | ASTM D-790 | 1.9%水｜120000 kg/cm2 |
| Rockwell hardness | | ASTM D-785 | 无水｜95 M-标度 |
| Rockwell hardness | | ASTM D-785 | 1.9%水｜- M-标度 |
| Rockwell hardness | | ASTM D-785 | 无水｜121 R-标度 |
| elongation at break | | ASTM D-638 | 无水｜5 % |
| elongation at break | | ASTM D-638 | 1.9%水｜5 % |
| IZOD impact strength | | ASTM D-256 | 无水｜12.5 kg·cm/cm |
| IZOD impact strength | | ASTM D-256 | 1.9%水｜15 kg·cm/cm |
| IZOD impact strength | | ASTM D-256 | 无水｜12.5 kg·cm/cm2 |
| IZOD impact strength | | ASTM D-256 | 1.9%水｜15 kg·cm/cm2 |
| IZOD impact strength | | ASTM D-256 | 无水｜15 kg·cm/cm |
| IZOD impact strength | | ASTM D-256 | 1.9%水｜20 kg·cm/cm |
| IZOD impact strength | | ASTM D-256 | 无水｜98 kg·cm/cm |
| shearing strength | | ASTM D-732 | 无水｜940 kg/cm2 |
| shearing strength | | ASTM D-732 | 1.9%水｜750 kg/cm2 |
| Rockwell hardness | | ASTM D-785 | 1.9%水｜- R-标度 |
| | ASTM D-790 | 无水｜2900 kg/cm2 |
| | ASTM D-790 | 1.9%水｜1850 kg/cm2 |
| | ASTM D-790 | 无水｜16000 kg/cm2 |
| | ASTM D-790 | 1.9%水｜- kg/cm2 |
| | ASTM D-790 | 无水｜3300 kg/cm2 |
| | ASTM D-790 | 1.9%水｜- kg/cm2 |
| tensile yield strength | | ASTM D-638 | 无水｜2000 kg/cm2 |
| tensile yield strength | | ASTM D-638 | 1.9%水｜1300 kg/cm2 |
| tensile yield strength | | ASTM D-638 | 无水｜1200 kg/cm2 |
| tensile yield strength | | ASTM D-638 | 1.9%水｜- kg/cm2 |
| tensile yield strength | | ASTM D-638 | 无水｜2900 kg/cm2 |
| tensile yield strength | | ASTM D-638 | 1.9%水｜- kg/cm2 |
| compressive strength | | ASTM D-695 | 无水｜1900 kg/cm2 |
| compressive strength | | ASTM D-695 | 1.9%水｜- kg/cm2 |
| compressive strength | | ASTM D-695 | 无水｜1000 kg/cm2 |
| compressive strength | | ASTM D-695 | 1.9%水｜- kg/cm2 |
| compressive strength | | ASTM D-695 | 无水｜2600 kg/cm2 |
| compressive strength | | ASTM D-695 | 1.9%水｜- kg/cm2 |
| Other performance | Test Condition | Test Method | Test Result |
|---|
| | | 无水｜45 wt% |
| | | 1.9%水｜- wt% |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Loss factor | | ASTM D-150 | 无水｜0.02 |
| Loss factor | | ASTM D-150 | 1.9%水｜0.06 |
| dielectric strength | | ASTM D-149 | 无水｜19 KV/mm |
| dielectric strength | | ASTM D-149 | 1.9%水｜15 KV/mm |
| dielectric constant | | ASTM D-150 | 无水｜4.2 |
| dielectric constant | | ASTM D-150 | 1.9%水｜4.5 |
| dielectric constant | | ASTM D-150 | 无水｜4.9 |
| dielectric constant | | ASTM D-150 | 1.9%水｜7.4 |
| Volume resistivity | | ASTM D-257 | 无水｜1015 Ω.cm |
| Volume resistivity | | ASTM D-257 | 1.9%水｜1012 Ω.cm |
| Loss factor | | ASTM D-150 | 无水｜0.03 |
| Loss factor | | ASTM D-150 | 1.9%水｜0.16 |
| arc resistance | | ASTM D-495 | 无水｜104 S |
| arc resistance | | ASTM D-495 | 1.9%水｜119 S |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| UL-94 flame retardant grade | | UL 94 | 无水｜HB |
| UL-94 flame retardant grade | | UL 94 | 1.9%水｜- |
| heat deflection temperature | | ASTM D-648 | 无水｜225 °C |
| heat deflection temperature | | ASTM D-648 | 1.9%水｜- °C |
| melting point | | 差示扫描测热计DSC | 225 °C |
| specific heat | | | 无水｜0.31 Cal/g·℃ |
| specific heat | | | 1.9%水｜- Cal/g·℃ |
| | ASTM D-696 | 无水｜2-3 ×10-5cm/cm/℃ |
| | ASTM D-696 | 1.9%水｜- ×10-5cm/cm/℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.