Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ISO 62 | 0.01 % |
| melt mass-flow rate | | ISO 1133 | 32 cm3/10min |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ISO 489 | 1.53 °C |
| transmittance | | ISO 13468-2 | 91 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527-2 | 63 Mpa |
| elongation at break | | ISO 527-2 | 4.5 % |
| Tensile modulus | | ISO 527-2 | 2600 Mpa |
| Charpy Notched Impact Strength | | ISO 179/1eA | 2.6 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 20 kJ/m² |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL -94 | HB 1.50mm |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC 60093 | 1E+14 Ω.cm |
| dielectric constant | | IEC 60250 | 2.35 1kHz |
| Dissipation Factor | | IEC 60112 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/Bf | 75 °C |
| vicat | | ISO 306/B50 | 80 °C |
| vicat | | ISO 11357-2 | 78 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare
View Prices