Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.57 g/cm³ |
| Apparent density | | ISO60 | 0.73 g/cm³ |
| Shrinkage rate | | ISO2577 | 0.65 % |
| Shrinkage rate | | ISO2577 | 0.35 % |
| Water absorption rate- | | ISO62 | 55.0 mg |
| PostShrinkage | | ISO2577 | 0.45 % |
| PostShrinkage | | ISO2577 | 0.45 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO2039-1 | 325 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| UL flame retardant rating | | UL94 | V-0 |
| UL flame retardant rating | | UL94 | V-0 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| CompressionMoldingPressure | | | >15.0 MPa |
| CompressionMoldingTemperature | | | 160到190 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179/1eU | 7.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 1.3 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2/1 | 10000 MPa |
| Tensile stress | | ISO527-2/5 | 50.0 MPa |
| Flexural modulus | | ISO178 | 9000 MPa |
| Bending stress | | ISO178 | 95.0 MPa |
| compression stress | | ISO604 | 250 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1E+11 ohms |
| Volume resistivity | | IEC60093 | 1E+12 ohms·cm |
| dielectric strength | | IEC60243-1 | 20 kV/mm |
| | IEC60250 | 14.0 |
| Dissipation Factor | | IEC60250 | 0.30 |
| CTI | | IEC60112 | 175 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/C | 135 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.