Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 7.5 g/10 min |
| Molten Volume Flow Rate (MVR) | | ISO 1133 | 6.00 cm3/10min |
| Shrinkage rate | | 内部方法 | 0.20 到 0.60 % |
| Shrinkage rate | | 内部方法 | 0.20 到 0.60 % |
| Water absorption rate | | ISO 62 | 0.15 % |
| Water absorption rate | | ISO 62 | 0.40 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 3950 Mpa |
| Tensile modulus | | ISO 527-2/1 | 3900 Mpa |
| tensile strength | | ASTM D638 | 55.0 Mpa |
| tensile strength | | ISO 527-2/5 | 54.0 Mpa |
| tensile strength | | ASTM D638 | 45.0 Mpa |
| tensile strength | | ISO 527-2/5 | 48.0 Mpa |
| elongation | | ASTM D638 | 4.3 % |
| elongation | | ISO 527-2/5 | 4.3 % |
| elongation | | ASTM D638 | 14 % |
| elongation | | ISO 527-2/5 | 8.7 % |
| Flexural modulus | | ASTM D790 | 3500 Mpa |
| Flexural modulus | | ISO 178 | 3450 Mpa |
| Bending stress | | ISO 178 | 98.0 Mpa |
| Bending stress | | ASTM D790 | 103 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam gap 7 | | ISO 179/1eA | 15 kJ/m² |
| Impact strength of simply supported beam gap 7 | | ISO 179/1eA | 25 kJ/m² |
| The impact strength of a simply supported beam without a notch is 7 | | ISO 179/1eU | 无断裂 |
| The impact strength of a simply supported beam without a notch is 7 | | ISO 179/1eU | 无断裂 |
| Unscented Izod Impact Strength 8 | | ISO 180/1U | 无断裂 |
| Unscented Izod Impact Strength 8 | | ISO 180/1U | 无断裂 |
| Dart impact equipped with measuring instruments | | ASTM D3763 | 40.0 J |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 120 °C |
| drying time | | | 3.0 到 4.0 hr |
| Suggested maximum moisture content | | | 0.020 % |
| Suggested injection volume | | | 40 到 60 % |
| Temperature at the rear of the barrel | | | 290 到 310 °C |
| Temperature in the middle of the barrel | | | 300 到 320 °C |
| Temperature at the front of the material cylinder | | | 310 到 330 °C |
| Spray nozzle temperature | | | 305 到 325 °C |
| Processing (melt) temperature | | | 310 到 330 °C |
| Temperature | | | 80 到 115 °C |
| Back pressure | | | 0.300 到 0.700 Mpa |
| screw speed | | | 40 到 70 rpm |
| Exhaust hole depth | | | 0.025 到 0.076 mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Thermal deformation temperature under load | | ASTM D648 | 137 °C |
| Thermal deformation temperature under load | | ISO 75-2/Ae | 135 °C |
| vicat | | ASTM D152510, ISO 306/B50, ISO 306/B120 | 146 °C |
| Ball Pressure Test | | IEC 60695-10-2 | 通过 |
| | ASTM E831, ISO 11359-2 | 4.7E-5 cm/cm/°C |
| | ASTM E831 | 7.0E-5 cm/cm/°C |
| | ISO 11359-2 | 7.0E-5 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.