EVOH EVAL™ C109B KURARAY JAPAN
669
- Properties:Lubricitycopolymer
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 190℃/2.16 kg | ISO 1133 | 9.3 | g/10 min |
| 210℃/2.16 kg | ISO 1133 | 21 | g/10 min | |
| Ethylene component | 35.0 | wt% |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M 计秤 | ISO 2039-2 | 94 | |
| Tensile modulus | ISO 527-2 | 2500 | Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 68.0 | Mpa |
| elongation | 断裂 | ISO 527-2 | 6.0 | % |
| Bending modulus | ISO 178 | 4800 | Mpa | |
| Impact strength of simply supported beam gap | ISO 179 | 1.0 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Glass transition temperature | DSC | DSC | 53.0 | °C |
| Melting temperature | ISO 3146 | 177 | °C | |
| Crystallization peak temperature | DSC | ISO 3146 | 154 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.