Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTM D955 | 1.2 % |
| Water absorption rate | | ASTM D570 | 0.020 % |
| density | | ASTM D792 | 1.42 g/cm³ |
| Shrinkage rate | | ASTM D955 | 0.32 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 118 |
| Rockwell hardness | M-Scale | ASTM D785 | 84 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 7500 MPa |
| Poisson's ratio | | | 0.37 |
| coefficient of friction | Steel - Dynamic | ASTM D1894 | 0.35 |
| coefficient of friction | Steel - Static | ASTM D1894 | 0.35 |
| elongation at break | | ASTM D790 | 3.4 % |
| tensile strength | | ASTM D638 | 135 MPa |
| elongation | Break | ASTM D638 | 2.1 % |
| Flexural modulus | | ASTM D790 | 6600 MPa |
| bending strength | | ASTM D790 | 180 MPa |
| compressive strength | | ASTM D695 | 170 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 100 J/m |
| Suspended wall beam without notch impact strength | | ASTM D256 | 650 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | ASTM D149 | 24 kV/mm |
| Volume resistivity | | ASTM D257 | 1E+16 ohms·cm |
| dielectric constant | | ASTM D150 | 4.00 |
| Dissipation Factor | | ASTM D150 | 2E-03 |
| arc resistance | | ASTM D495 | 120 sec |
| Compared to the Leakage Tracking Index (CTI) | | ASTM D3638 | PLC 3 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | ASTM D696 | 3.5E-05 cm/cm/°C |
| Heat distortion temperature | | ASTM D648 | 230 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 3.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.