PCTG AE850
49
- Usages:currency
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ISO 1133 | 10 g/10 min | |
| Melt volume flow rate | ISO 1133 | 11.0 cm3/10min | |
| melt mass-flow rate | ISO 1133 | 10 g/10min | |
| Melt volume flow rate | ISO 1133 | 10.6 cm3/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | 68 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | 68 R 计秤 | ||
| tensile strength | ISO 527-2/5 | 29.0 Mpa | |
| Flexural modulus | ISO 178 | 1450 Mpa | |
| bending strength | ISO 178 | 47.0 Mpa | |
| Charpy Notched Impact Strength | ISO 179 | 35 kJ/m² | |
| tensile strength | ISO 527-2/50 | 29.0 Mpa | |
| Flexural modulus | ISO 178 | 1450 Mpa | |
| bending strength | ISO 178 | 46.8 Mpa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature (HDT) | ISO 75-2/A | 74.0 °C | |
| vicat | ISO 306/B | 89.0 °C | |
| Hot deformation temperature (HDT) | ISO 75-2/A | 74.3 °C | |
| vicat | ISO 306/B | 88.8 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.