Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTMD1238 | 6.0 g/10min |
| Melt volume flow rate | | ISO1133 | 6.00 cm3/10min |
| Melt volume flow rate | | ISO1133 | 65.0 cm3/10min |
| flow | | ASTMD955 | 0.20到0.60 % |
| Water absorption rate | | ASTMD570,ISO62 | 0.10 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| R-level | | ASTMD785 | 62 |
| R scale | | ISO2039-2 | 62 |
| | ISO2039-1 | 35.0 Mpa |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| --2 | | ASTMD542 | 1.570 |
| transmissivity | | ASTMD1003 | 91.0 % |
| Haze ratio | | ASTMD1003 | 2.0 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| fracture | | ASTMD638 | 70 % |
| Fracture, 23 ° C | | ISO527-2 | 120 % |
| | ASTMD638 | 23.4 Mpa |
| | ISO527-2 | 28.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179 | 无断裂 |
| 23°C | | ASTMD256 | 590 J/m |
| 23°C | | ISO180/A | 15 kJ/m² |
| | ISO180 | 200 kJ/m² |
| Falling hammer impact | | ASTMD5420 | 19.2 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| 0.45MPa, annealing | | ISO75-2/B | 78.0 °C |
| 1.8MPa, annealing | | ISO75-2/B | 86.1 °C |
| 1.8MPa, annealing | | ISO75-2/A | 67.0 °C |
| maximum service temperature | | | 250 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.