Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Thermosetting components | | | 按重量计算的混合比:100.按容量计算的混合比:100 |
| Thermosetting components | | | 按重量计算的混合比:22.按容量计算的混合比:25 |
| Thermosetting mixed viscosity | | ASTM D4878 | 25000to35000 cP |
| stripping time | | 内部方法 | 360to720 min |
| stripping time | | 内部方法 | 120to240 min |
| GelTime | | ASTM D2971 | 32.0 min |
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D4669 | 1.10 g/cm³ |
| Shrinkage rate | | ASTM D2566 | 0.050to0.20 % |
| Weight Percubicinch | | | 18 g |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 77to83 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | ASTM D790 | 49.0 MPa |
| Tensile modulus | | ASTM D638 | 179 MPa |
| tensile strength | | ASTM D638 | 33.8 MPa |
| elongation | Break | ASTM D638 | 16 % |
| Flexural modulus | | ASTM D790 | 917 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 20 J/m |
| Suspended wall beam without notch impact strength | | ASTM D256 | 110 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 80.0 °C |
| Heat distortion temperature | | ASTM D648 | 94.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.