Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 10 g/10min |
| melt mass-flow rate | | ASTM D1238 | 22 g/10min |
| Shrinkage rate | | 内部方法 | 0.40-0.60 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 111 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | ASTM D523 | 98 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | ISO 3795 | 39 mm/min |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Dart impact | | ASTM D3763 | 33.9 J |
| Dart impact | | ASTM D3763 | 22.6 J |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 3030 Mpa |
| tensile strength | | ASTM D638 | 60.7 Mpa |
| tensile strength | | ASTM D638 | 44.1 Mpa |
| elongation | | ASTM D638 | 3.7 % |
| elongation | | ASTM D638 | 36 % |
| Flexural modulus | | ASTM D790 | 2550 Mpa |
| bending strength | | ASTM D790 | 86.2 Mpa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 107 °C |
| Heat distortion temperature | | ASTM D648 | 90.0 °C |
| vicat | | ASTM D15256 | 121 °C |
| Linear coefficient of thermal expansion | | ASTME831 | 9E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ASTME831 | 8.1E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.