PA6 73G50HSLA BK416 DUPONT USA

Form：Granules

Properties:

High glosslubricationGood appearance

Typical Applications:

Electronic and Electrical ApplicationsWear resistant accessorieshousehold electrical appliances

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electronic and Electrical Applications \| Wear resistant accessories \| household electrical appliances
Properties:	High gloss \| lubrication \| Good appearance

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	100	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	100	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning rate	1.00mm	ISO 3795	31	mm/min
Flammability level	1.5mm	IEC 60695-11-10,-20	HB
FMVSS flammability		FMVSS302	B
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2	15500	Mpa
tensile strength	Break	ISO 527-2	233	Mpa
Tensile strain	Break	ISO 527-2	2.2	%
Tensile creep modulus	1hr	ISO 899-1	--	Mpa
Tensile creep modulus	Tensile creep modulus	1000hr	ISO 899-1	--	Mpa
Bending modulus		ISO 178	14300	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	219	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	212	°C
Vicat softening temperature		ISO 306/B50	215	°C
Melting temperature		ISO 11357-3	219	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	1.5E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	1E-04	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	TD	ISO 294-4	0.60	%
MediumDensity			1.24	g/cm³
SpecificHeatCapacity of Melt			2050	J/kg/°C
ThermalConductivityofMelt			0.26	W/m/K
Shrinkage rate	MD	ISO 294-4	0.30	%
Water absorption rate	Saturation,23°C,2.00mm	ISO 62	4.5	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	1.5	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	--	ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.