Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.45 g/cm³ |
| Water absorption rate | | ASTM D570 | 0.10 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 81 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| coefficient of friction | Itself - Static | ASTM D1894 | 0.10 |
| bending strength | Yield | ASTM D790 | 124 MPa |
| coefficient of friction | Itself - Dynamic | ASTM D1894 | 0.080 |
| Tensile modulus | | ASTM D638 | 2760 MPa |
| tensile strength | Break | ASTM D638 | 72.4 MPa |
| elongation | Break | ASTM D638 | 4.0 % |
| Flexural modulus | | ASTM D790 | 3240 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 32 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 171 °C |
| Glass Transition Temperature | | DSC | 143 °C |
| melting temperature | | DSC | 343 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.