PPO FE1520PW-801 SABIC INNOVATIVE NETHERLANDS

Form：Granules | Grade：Food grade

Properties:

Low water absorptionHot water resistance

Typical Applications:

valveFaucetWater pump impellershower head

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	valve \| Faucet \| Water pump impeller \| shower head
Properties:	Low water absorption \| Hot water resistance

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	30	kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	4.0	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	6.0	kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	23	kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	25	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ASTM D638	7110	Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	7180	Mpa
tensile strength	Break	ASTM D638	119	Mpa
tensile strength	tensile strength	Break	ISO 527-2/5	119	Mpa
elongation	Break	ASTM D638	2.6	%
Tensile strain	Break	ISO 527-2/5	2.6	%
Bending modulus	50.0mmSpan	ASTM D790	6970	Mpa
Bending modulus	Bending modulus		ISO 178	6040	Mpa
bending strength		ISO 178	165	Mpa
bending strength	bending strength	Break,50.0mmSpan	ASTM D790	175	Mpa
Taber abraser	1000Cycles,1000g,CS-17Wheel	Internal Method	65.0	mg
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed,100mmSpan	ISO 75-2/Be	139	°C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	135	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,100mmSpan	ISO 75-2/Ae	132	°C
Vicat softening temperature	--	ISO 306/A50	150	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	144	°C
Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	3E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	7E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Melt Volume Flow Rate (MVR)	280°C/10.0kg	ISO 1133	22.0	cm3/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.20-0.40	%
Shrinkage rate	Shrinkage rate	TD：3.20mm	Internal Method	0.30-0.60	%
Water absorption rate	Saturation,23°C	ISO 62	0.20	%
Water absorption rate	Water absorption rate	Equilibrium,50%RH	ASTM D570	0.060	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test	H358/30	ISO 2039-1	220	Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.