| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ISO62 | 0.22 % |
| density | | ASTMD792 | 1.04 g/cm³ |
| density | | ISO1183 | 1.04 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 1.5 g/10min |
| melt mass-flow rate | | ASTMD1238 | 19 g/10min |
| Melt volume flow rate | | ASTMD1238 | 4.80 cm3/10min |
| Melt volume flow rate | | ISO1133 | 19.0 cm3/10min |
| Shrinkage rate | | ASTMD955 | 0.40to0.70 % |
| Shrinkage rate | | ISO294-4 | 0.40to0.70 % |
| Water absorption rate | | ASTMD570 | 1.0 % |
| Water absorption rate | | ISO62 | 1.0 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTMD785 | 103 |
| | ISO2039-1 | 97.0 Mpa |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| Yellowness Index | | DIN6167 | 13 YI |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTMD638 | 2300 Mpa |
| Tensile modulus | | ISO527-2 | 2300 Mpa |
| tensile strength | | ASTMD638 | 45.0 Mpa |
| Tensile stress | | ISO527-2 | 45.0 Mpa |
| Tensile strain | | ISO527-2 | 2.6 % |
| elongation | | ASTMD638 | 2.6 % |
| Nominal tensile fracture strain | | ISO527-2 | 10 % |
| Flexural modulus | | ASTMD790 | 2300 Mpa |
| bending strength | | ASTMD790 | 65.0 Mpa |
| Bending stress | | ISO178 | 65.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179 | 8.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO179 | 22 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179 | 100 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179 | 180 kJ/m² |
| Impact strength of cantilever beam gap | | ASTMD256 | 59 J/m |
| Impact strength of cantilever beam gap | | ASTMD256 | 100 J/m |
| Impact strength of cantilever beam gap | | ASTMD256 | 300 J/m |
| Impact strength of cantilever beam gap | | ISO180/A | 8.0 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/A | 26 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1E+13 ohms |
| Volume resistivity | | ASTMD257 | >1.0E+15 ohms·cm |
| Volume resistivity | | IEC60093 | 1E+15 ohms·cm |
| dielectric constant | | ASTMD150 | 2.80 |
| | IEC60250 | 2.90 |
| | IEC60250 | 2.80 |
| Dissipation Factor | | IEC60250 | 4.8E-03 |
| Dissipation Factor | | IEC60250 | 7.9E-03 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO11359-2 | 8.0E-5to1.1E-4 cm/cm/°C |
| thermal conductivity | | DIN52612 | 0.17 W/m/K |
| | ASTMD648 | 90.6 °C |
| | ASTMD648 | 104 °C |
| | ISO75-2/B | 99.0 °C |
| | ASTMD648 | 77.8 °C |
| | ASTMD648 | 98.9 °C |
| | ISO75-2/A | 94.0 °C |
| vicat | | ISO306/A50 | 105 °C |
| vicat | | ISO306/B50 | 96.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.