PEEK AV-750 SOLVAY USA

Form：Granules | Grade：Injection grade

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Certificates

No Data...

Technical Data Sheet

Filling analysis	Test Condition	Test Method	Test Result	Test Unit
Melt viscosity	400°C, 1000 sec^-1	ASTM D3835	450	Pa·s
impact performance	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength	--	ASTM D4812	590	J/m
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	--	ISO 180	41	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.8 mm	UL 94	V-1
UL flame retardant rating	UL flame retardant rating	1.6 mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	--5	ASTM D638	15100	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1A/1	16700	Mpa
tensile strength	Yield, 5.00 mm	ISO 527-2/1A/5	188	Mpa
tensile strength	tensile strength	--6	ASTM D638	191	Mpa
elongation	Break5	ASTM D638	1.8	%
elongation	elongation	Break	ISO 527-2/1A/5	1.8	%
Bending modulus	--	ASTM D790	14800	Mpa
Bending modulus	Bending modulus	--	ISO 178	15400	Mpa
bending strength	23°C	ASTM D790	253	Mpa
	bending strength	250°C	ASTM D790	54.0	Mpa
	bending strength	bending strength	--	ISO 178	250	Mpa
compressive strength		ASTM D695	182	Mpa
shear strength		ASTM D732	89.0	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			150 to 175	°C
drying time			2.5 to 4.0	hr
Processing (melt) temperature			370 to 395	°C
Mold temperature			175 to 210	°C
Back pressure			0.138 to 0.345	Mpa
Screw speed			75	rpm
Screw compression ratio			2.0:1.0
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8 MPa, Annealed	ASTM D648	285	°C
Glass transition temperature		ASTM D3418	150	°C
Melting temperature		ASTM D3418	345	°C
Linear coefficient of thermal expansion	-50 to 50°C，Flow	ASTM E831	1.5E-5	cm/cm/°C
specific heat	50°C	DSC	1260	J/kg/°C
specific heat	specific heat	200°C	DSC	1620	J/kg/°C
thermal conductivity		ASTM E1530	0.31	W/m/K
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	380°C/2.16 kg	ASTM D1238	7.0	g/10 min
Shrinkage rate	Flow : 3.18 mm	ASTM D955	0.10 - 0.30	%
Shrinkage rate	Shrinkage rate	Across FlowFlow : 3.18 mm	ASTM D955	1.2 - 1.4	%
Water absorption rate	24 hr	ASTM D570	0.10	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		ASTM D257	> 1.9E+17	ohms
Volume resistivity		ASTM D257	1.8E+17	ohms·cm
Dielectric strength		ASTM D149	19	KV/mm
Dielectric constant	60 Hz	ASTM D150	3.68
	Dielectric constant	1 kHz	ASTM D150	3.69
	Dielectric constant	Dielectric constant	1 MHz	ASTM D150	3.66
Dissipation factor	60 Hz	ASTM D150	2.0E-3
	Dissipation factor	1 kHz	ASTM D150	1.0E-3
	Dissipation factor	Dissipation factor	1 MHz	ASTM D150	3.0E-3
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Scale	ASTM D785	105

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.