| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 0.930 g/cm³ |
| Water absorption rate | | ASTM D570 | <0.010 % |
| Water absorption rate | Saturation | ASTM D570 | <0.010 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 66 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| limiting pv value | | 内部方法 | 0.0701 MPa·m/s |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 689 MPa |
| tensile strength | Ultimate | ASTM D638 | 40.0 MPa |
| elongation | Break | ASTM D638 | 300 % |
| compressive strength | | ASTM D695 | 20.7 MPa |
| shear strength | | ASTM D732 | 33.1 MPa |
| coefficient of friction | Steel - Static | 内部方法 | 0.12 |
| Flexural modulus | | ASTM D790 | 758 MPa |
| bending strength | Yield | ASTM D790 | 24.1 MPa |
| Compression Modulus | | ASTM D695 | 552 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256A | 无断裂 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | ASTM D149 | 91 kV/mm |
| dielectric constant | | ASTM D150 | 2.30 |
| Dissipation Factor | | ASTM D150 | 5E-04 |
| Surface Resistivity | | ASTM D257 | >1.0E+15 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 46.7 °C |
| Maximum operating temperature LongTerm, Air | | | 82 °C |
| Crystallization peak temperature | | ASTM D3418 | 135 °C |
| Linear coefficient of thermal expansion | | ASTME831 | 2.2E-04 cm/cm/°C |
| thermal conductivity | | | 0.41 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.