PA6

PA6 Durethan® BKV35Q 901510 ENVALIOR WUXI

Properties:
Filler: Glass fiber reinf35% filler by weight
Compare View Prices

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	70 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	80 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	70 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	75 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.6mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	3.2mm	UL 94	HB
Burning wire flammability index	2.0mm	IEC 60695-2-12	650 °C
Extreme Oxygen Index		ISO 4589-2	23 %
BurningBehavior	>1.00mm	ISO 3795	passed

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus	23°C	ISO 178/A	10700 Mpa
bending strength	3.5%Strain	ISO 178/A	280 Mpa
bending strength	bending strength	23°C	ISO 178	290 Mpa
Tensile creep modulus	1000hr	ISO 899-1	-- Mpa
Tensile creep modulus	Tensile creep modulus	1hr	ISO 899-1	-- Mpa
Tensile strain	Break,23°C	ISO 527-2/5	3.0 %
tensile strength	Break,23°C	ISO 527-2/5	180 Mpa
Tensile modulus	23°C	ISO 527-2/1	10700 Mpa
bending strength	FlexuralStrainatFlexuralStrength5(23°C)		4.0 %

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	8E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	2E-05 cm/cm/°C
Melting temperature		ISO 11357-3	222 °C
Vicat softening temperature	--	ISO 306/B120	>200 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	200 °C
Hot deformation temperature	8.0MPa,Unannealed	ISO 75-2/C	150 °C
	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	205 °C
	Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	215 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.9 %
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	6.5 %
Shrinkage rate	MD:120°C,2hr,2.00mm3	ISO 294-4	0.070 %
	Shrinkage rate	MD:280°C,2.00mm2	ISO 294-4	0.23 %
		Shrinkage rate	TD:120°C,2hr,2.00mm3	ISO 294-4	0.14 %
		Shrinkage rate	Shrinkage rate	TD:280°C,2.00mm2	ISO 294-4	0.70 %
Apparent density		ISO 60	0.70 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity	23°C	IEC 60093	1E+15 ohms·cm
Surface resistivity		IEC 60093	1E+14 ohms
Dielectric strength	23°C,1.00mm	IEC 60243-1	40 KV/mm
Relative permittivity	23°C,100Hz	IEC 60250	4.00
Relative permittivity	Relative permittivity	23°C,1MHz	IEC 60250	4.00
Dissipation factor	23°C,100Hz	IEC 60250	7E-03
Dissipation factor	Dissipation factor	23°C,1MHz	IEC 60250	0.015
Compared to the anti leakage trace index	SolutionA	IEC 60112	V

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test		ISO 2039-1	230 Mpa

film	Test Condition	Test Method	Test Result
Thin film puncture strength	--7	ISO 6603-2	1060 N
	Thin film puncture strength	--6	ISO 6603-2	3.30 J
		Thin film puncture strength	--7	ISO 6603-2	3.90 J
		Thin film puncture strength	Thin film puncture strength	--6	ISO 6603-2	945 N

Supplementary Information	Test Condition	Test Method	Test Result
ISO Shortcut		ISO 1874	PA6.GR.14-110.GF35

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

PA6 Durethan® BKV35Q 901510 ENVALIOR WUXI