HIPS 9200

Properties:
Low speed solidification point
excellent printability
good micro adjustability
high resistance to stress cracking
and high impact resistance
Usages:
Sheet and lithography printing
Compare

Technical Data Sheet

physical property	Test Method	Test Result
density	ASTM D-792	1.04 g/cm3
Apparent density	ASTM D-792	0.59-0.64 g/cm3
melt mass-flow rate	ASTM D-1238	2.5 g/10min
Shrinkage rate	ASTM D-955	0.40-0.70 %

optical performance	Test Condition	Test Method	Test Result
gloss		ASTM D-523	10

Mechanical properties	Test Method	Test Result
Rockwell hardness	ASTM D-785	42 L Scale
Tensile modulus	ASTM D-638	1690 MPa
tensile strength	ASTM D-638	19.0 MPa
elongation at break	ASTM D-638	40 %
Flexural modulus	ASTM D-790	1660 MPa
bending strength	ASTM D-790	39.0 MPa
Impact strength of cantilever beam gap	ASTM D-256	123 J/m

Electrical performance	Test Condition	Test Method	Test Result
dielectric strength		ASTM D-149	16 kV/mm
dielectric constant		ASTM D-150	2.50

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ASTM D-648	86.0 ℃
vicat		ASTM D-1525	102 ℃
Linear coefficient of thermal expansion	Flow	ASTM D-696	0.000090 ℃

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.