Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.01 g/cm³ |
| melt mass-flow rate | | JISK6719 | 20 g/10min |
| Water absorption rate | Equilibrium | ASTM D570 | <0.010 % |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | ASTM D1003 | 92.0 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 2200 MPa |
| tensile strength | | ISO 527-2 | 53.0 MPa |
| Tensile strain | Break | ISO 527-2 | 90 % |
| Flexural modulus | | ISO 178 | 2100 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 60 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | ASTM D150 | 2.30 |
| Dissipation Factor | | ASTM D150 | <1.0E-3 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | JISK7121 | 102 °C |
| Linear coefficient of thermal expansion | | ASTME831 | 7E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare