PA6 LUBEMID B27 EL80 NATURAL

Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
density		ISO 1183/A	1.05to1.09 g/cm³

flammability	Test Condition	Test Method	Test Result
Burning wire flammability index		IEC 60695-2-12	650 °C

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap		ASTM D256	50to60 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ISO 180/A	55to60 kJ/m²
Suspended wall beam without notch impact strength		ISO 180	无断裂
Impact strength of simply supported beam without notch		ISO 179/1eU	无断裂
Impact strength of cantilever beam gap		ASTM D256A	500to600 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256	无断裂
Charpy Notched Impact Strength		ISO 179/1eA	45to55 kJ/m²

Mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/1A/1	2200to2600 MPa
tensile strength	Yield	ISO 527-2/1A/50	45.0to55.0 MPa
tensile strength	tensile strength	Break	ISO 527-2/1A/50	40.0to50.0 MPa
Tensile strain	Yield	ISO 527-2/1A/50	10to20 %
Tensile strain	Tensile strain	Break	ISO 527-2/1A/50	35to40 %
Flexural modulus		ISO 178	1500to2000 MPa
bending strength		ISO 178	45.0to55.0 MPa

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ASTM D648	160to170 °C
	Heat distortion temperature		ISO 75-2/B	165to175 °C
	Heat distortion temperature	Heat distortion temperature		ASTM D648	55.0to65.0 °C
vicat		ISO 306/A120	195to205 °C
vicat	vicat		ISO 306/B120	205to215 °C
melting temperature		内部方法	210to225 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.