PBT/PTFE LNP™ LUBRICOMP™ WL-4540-NAT

Properties:
wear resistant
Usages:
Aerospace Applications
Compare
View Prices

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
Shrinkage rate		ASTMD955	1.0to3.0 %
Shrinkage rate	Shrinkage rate		ASTMD955	1.0to3.0 %
Water absorption rate		ASTMD570	0.050 %
Water absorption rate	Water absorption rate		ISO62	0.090 %

Mechanical properties	Test Condition	Test Method	Test Result
Tensile stress		ISO527-2/5	37.0 Mpa
elongation		ASTMD638	11 %
Tensile strain		ISO527-2/5	11 %
elongation		ASTMD638	11 %
Tensile strain		ISO527-2/5	12 %
Flexural modulus		ASTMD790	2190 Mpa
Flexural modulus	Flexural modulus		ISO178	2130 Mpa
Bending stress		ISO178	64.0 Mpa
		ASTMD3702Modified	0.24
			ASTMD3702Modified	0.13
Tensile modulus		ASTMD638	2280 Mpa
Tensile modulus	Tensile modulus		ISO527-2/1	2240 Mpa
tensile strength		ASTMD638	37.0 Mpa
Tensile stress		ISO527-2/5	37.0 Mpa
tensile strength		ASTMD638	37.0 Mpa
Wear factor - Washer		ASTMD3702Modified	16.0 10^-10in^5-min/ft-lb-hr

Impact resistance	Test Method	Test Result
Suspended wall beam notch impact strength 6	ISO180/1A	3.7 kJ/m²
Unscented Izod Impact Strength 5	ISO180/1U	20 kJ/m²
Dart impact equipped with measuring instruments	ASTMD3763	2.20 J
Multi axis Instrumented Impact Energy	ISO6603-2	0.700 J

Thermal performance	Test Method	Test Result
	ASTMD648	182 °C
Hot deformation temperature 7	ISO75-2/Bf	158 °C
	ASTMD648	55.4 °C
Hot deformation temperature 7	ISO75-2/Af	54.0 °C
	ASTMD696	6.8E-05 cm/cm/°C
		ASTMD696	1.1E-04 cm/cm/°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

PBT/PTFE LNP™ LUBRICOMP™ WL-4540-NAT