Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | | 1.40 g/cm³ |
| Shrinkage rate | | | 0.0 % |
| Shrinkage rate | | | 0.20 % |
| Water absorption rate | Equilibrium | ASTM D570 | 0.23 % |
| spiral flow length | | ASTM D3123 | 3.70 cm |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 95 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 230 MPa |
| elongation | | ASTM D638 | 3.7 % |
| Tensile modulus | | ASTM D638 | 28500 MPa |
| Flexural modulus | | ASTM D790 | 28800 MPa |
| bending strength | | ASTM D790 | 380 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 45 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 358 °C |
| Continuous use temperature | | UL 746B | 300 °C |
| Glass Transition Temperature | | ASTM D3418 | 152 °C |
| melting temperature | | ASTM D3418 | 372 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.