Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | 内部方法 | 0.50 到 0.70 % |
| Shrinkage rate | | 内部方法 | 0.50 到 0.70 % |
| Water absorption rate | | ISO 62 | 0.20 % |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | ASTM D1003 | 41.0 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1 | 2400 Mpa |
| Tensile stress | | ISO 527-2/50 | 61.0 Mpa |
| Tensile stress | | ISO 527-2/50 | 56.0 Mpa |
| Tensile strain | | ISO 527-2/50 | 6.0 % |
| Nominal tensile fracture strain | | ISO 527-2/50 | > 50 % |
| Bending modulus 2 | | ISO 178 | 2230 Mpa |
| Bending stress 2 | | ISO 178 | 93.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179 | 无断裂 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | > 1.0E+15 ohms |
| Volume resistivity | | IEC 60093 | > 1.0E+15 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO 75-2/B | 141 °C |
| | ISO 75-2/A | 129 °C |
| vicat | | ISO 306/B50 | 148 °C |
| | ISO 11359-2 | 7.0E-5 cm/cm/°C |
| | ISO 11359-2 | 7.0E-5 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.