Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.20 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 7.0 g/10 min |
| Shrinkage rate - flow | | ASTM D955 | 0.50 到 0.70 % |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ASTM D542 | 1.585 |
| transmissivity | | ASTM D1003 | 89.0 % |
| Haze ratio | | ASTM D1003 | < 0.80 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 61.8 Mpa |
| elongation | | ASTM D638 | > 100 % |
| | ASTM D790 | 2350 Mpa |
| bending strength | | ASTM D790 | 90.2 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 830 J/m |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 120 °C |
| drying time | | | 4.0 hr |
| Suggested maximum moisture content | | | 0.020 % |
| Suggested maximum recycled material ratio | | | 20 % |
| Hopper temperature | | | 60 到 80 °C |
| Temperature at the rear of the barrel | | | 290 到 310 °C |
| Temperature in the middle of the barrel | | | 280 到 300 °C |
| Temperature at the front of the material cylinder | | | 270 到 290 °C |
| Spray nozzle temperature | | | 280 到 300 °C |
| Processing (melt) temperature | | | 290 到 310 °C |
| Temperature | | | 60 到 90 °C |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Thermal deformation temperature under load | | ASTM D648 | 144 °C |
| Thermal deformation temperature under load | | ASTM D648 | 133 °C |
| vicat | | ASTM D15255 | 153 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.