EAA 1321 STYRON US

Form：Granules | Grade：Blow molding grade

Properties:

Heat sealing performanceResistance to stress crachigh strengthHigh toughness

Typical Applications:

Food service sectorFood packagingFood containersMulti layer composite material food packaging

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Food service sector \| Food packaging \| Food containers \| Multi layer composite material food packaging
Properties:	Heat sealing performance \| Resistance to stress crac \| high strength \| High toughness

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
gloss	45°，50.8um	ASTM D-2457	76
turbidity	50.8um	ASTM D-1003	3.7	%
turbidity	turbidity	50.8um	ISO 14782	3.7	%
gloss	45°,50.8μm	ASTM D2457	76
turbidity	50.8μm	ISO 14782	3.7	%
turbidity	turbidity	50.8μm	ASTM D1003	3.7	%
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	190℃/2.16kg	ASTM D-1238	2.6	g/10min
melt mass-flow rate	melt mass-flow rate	190℃/2.16kg	ISO 1133	2.6	g/10min
Monomer content		Internal Method	6.5	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Yield,Compression Molded	ASTM D-638	10	MPa
	tensile strength	Yield,Compression Molded	ISO 527-2/508	10	MPa
		tensile strength	Compression Molded，Break	ASTM D-638	20.1	MPa
			tensile strength	50.8um，TD,Break	ISO 527-3	31.8	MPa
			tensile strength	tensile strength	50.8um，MD,Break	ISO 527-3	31.8	MPa
Elongation at Break	50.8um，TD	ASTM D-882	510	%
	Elongation at Break	50.8um，MD	ASTM D-882	460	%
		Elongation at Break	50.8um，MD	ISO 527-3	460	%
		Elongation at Break	Elongation at Break	50.8um，TD	ISO 527-3	510	%
Dart impact	50.8um	ASTM D-1709B	410	g
Dart impact	Dart impact	50.8um	ISO 7765-1/B	410	g
Elmendorf tear strength	50.8um，MD	ASTM D-1922	270	g
Elmendorf tear strength	Elmendorf tear strength	50.8um，TD	ASTM D-1922	390	g
tensile strength	Compression Molded，Break	ISO 527-2/508	20.1	MPa
Elongation at Break	Compression Molded	ASTM D-638	640	%
Elongation at Break	Elongation at Break	Compression Molded	ISO 527-2/508	640	%
tensile strength	50.8um，Yield,MD	ASTM D-882	11.3	MPa
	tensile strength	50.8um，Yield,TD	ASTM D-882	11.1	MPa
		tensile strength	50.8um，Yield,MD	ISO 527-3	11.3	MPa
			tensile strength	50.8um，Yield,TD	ISO 527-3	11.5	MPa
				tensile strength	50.8um，TD,Break	ASTM D-882	31.8	MPa
				tensile strength	tensile strength	50.8um，MD,Break	ASTM D-882	31.8	MPa
Elmendorf tear strength	50.8um，MD	ISO 6383-2	1200	N
Elmendorf tear strength	Elmendorf tear strength	50.8um，TD	ISO 6383-2	1700	N
elongation	Break,Compression Molded	ISO 527-2/508	640	%
elongation	elongation	Break,Compression Molded4	ASTM D638	640	%
tensile strength	Break,Compression Molded	ISO 527-2/508	20.1	Mpa
	tensile strength	Break,Compression Molded4	ASTM D638	20.1	Mpa
		tensile strength	Yield,Compression Molded	ISO 527-2/508	10.0	Mpa
		tensile strength	tensile strength	Yield,Compression Molded4	ASTM D638	10.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature		ASTM D-1525	88.9	℃
Vicat softening temperature	Vicat softening temperature		ISO 306	88.9	℃
Melting temperature	DSC		103	℃
Vicat softening temperature		ASTMD1525	88.9	°C
Melting temperature		Internal Method	103	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D-792	0.935	g/cm³
density	density		ISO 1183/A	0.935	g/cm³
Content of comonomer		Internal Method	6.5	%
melt mass-flow rate	190°C/2.16kg	ASTMD1238	2.6	g/10min
density		ASTMD792	0.935	g/cm³
film	Test Condition	Test Method	Test Result	Test Unit
Elmendorf tear strength	TD:51μm	ASTM D1922	390	g
	Elmendorf tear strength	MD:51μm	ISO 6383-2	1200	N
	Elmendorf tear strength	Elmendorf tear strength	TD:51μm	ISO 6383-2	1700	N
tensile strength	MD:Yield,51μm	ASTM D882	11.3	Mpa
	tensile strength	TD:Yield,51μm	ASTM D882	11.1	Mpa
		tensile strength	MD:Yield,51μm	ISO 527-3	11.3	Mpa
			tensile strength	TD:Yield,51μm	ISO 527-3	11.5	Mpa
				tensile strength	MD:Break,51μm	ASTMD882	31.8	Mpa
				tensile strength	tensile strength	TD:Break,51μm	ASTMD882	31.8	Mpa
elongation	MD:Break,51μm	ASTMD882	460	%
elongation	elongation	TD:Break,51μm	ASTMD882	510	%
Dart impact	51μm	ASTMD1709B	410	g
Elmendorf tear strength	MD:51μm	ASTM D1922	270	g

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.