Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTMD955 | 1.8到2.1 % |
| density | | ASTMD792 | 1.41 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 13 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTMD785 | 82 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | | ASTMD638 | 60 % |
| Flexural modulus | | ASTMD790 | 2550 MPa |
| bending strength | | ASTMD790 | 90.2 MPa |
| tensile strength | | ASTMD638 | 61.3 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 64 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTMD257 | 1E+16 ohms |
| Volume resistivity | | ASTMD257 | 1E+14 ohms·cm |
| dielectric strength | | ASTMD149 | 24 kV/mm |
| Dissipation Factor | | ASTMD150 | 3.8E-04 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTMD648 | 160 °C |
| Heat distortion temperature | | ASTMD648 | 110 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.