PPO N1250 BK1066 SABIC INNOVATIVE SHANGHAI

123

Form：Granules | Grade：Injection grade

Properties:

High temperature resistanHigh mobilityGlass fiber reinforced

Typical Applications:

Automotive interior partsElectrical applications

Supplier(4)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive interior parts \| Electrical applications
Properties:	High temperature resistan \| High mobility \| Glass fiber reinforced

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C, Total Energy	ASTM D3763	40.0	J
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.40 mm	UL 94	V-2
	UL flame retardant rating	0.76 mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	2.5 mm	UL 94	5VA
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	Yield, 50.0 mm Span	ASTM D790	113	Mpa
Bending modulus	50.0 mm Span	ASTM D790	2680	Mpa
elongation	Break	ASTM D638	25	%
elongation	elongation	Yield	ASTM D638	4.6	%
tensile strength	Break	ASTM D638	64.0	Mpa
tensile strength	tensile strength	Yield	ASTM D638	75.0	Mpa
Tensile modulus		ASTM D638	2680	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			105 to 110	°C
drying time			3.0 to 4.0	hr
Suggested maximum moisture content			0.020	%
Suggested injection volume			30 to 70	%
Temperature at the rear of the barrel			245 to 295	°C
Temperature in the middle of the barrel			255 to 300	°C
Temperature at the front of the material cylinder			265 to 305	°C
Spray nozzle temperature			275 to 305	°C
Processing (melt) temperature			275 to 305	°C
Mold temperature			70 to 100	°C
Back pressure			0.300 to 0.700	Mpa
Screw speed			20 to 100	rpm
Exhaust hole depth			0.038 to 0.051	mm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	6.8E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	6.1E-5	cm/cm/°C
Vicat softening temperature		ASTM D15255	137	°C
Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	122	°C
	Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	116	°C
		Hot deformation temperature	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	133	°C
		Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	131	°C
RTI		UL 746	115	°C
RTI Imp		UL 746	105	°C
RTI Elec		UL 746	110	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.70	%
melt mass-flow rate	300°C/5.0 kg	ASTM D1238	28	g/10 min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Hot wire ignition		UL 746	PLC 0
High Voltage Arc Resistance Index (HVAR) (PLC)		UL 746	PLC 4
High arc combustion index		UL 746	PLC 0
Compared to the anti leakage trace index		UL 746	PLC 2
Arc resistance		ASTM D495	PLC 6

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PPO N1250 BK1066 SABIC INNOVATIVE SHANGHAI

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index